Influence of carbon content on the microstructure,

Acta Materialia. 61, 558-578 (2013)

관리자 | 2013.10.25 12:00 | 조회 4463






We report on the effects of carbon content on the martensitic transformation and its contribution to the work-hardening behavior of Fe–Mn–C steels during tensile deformation based on analysis by X-ray diffraction, electron backscatter diffraction and transmission electron microscopy. Austenite/ε-martensite dual-phase Fe–17Mn–C (wt.%) steels containing different carbon contents (0.01, 0.10, 0.20 wt.%) were investigated before, during and after tensile deformation. Before deformation, the transformation of austenite to thermally induced ε-martensite on cooling was suppressed as the carbon content increases. To precisely monitor microstructural changes during deformation, stepwise loading experiments were carried out in combination with electron backscatter diffraction analysis. This approach revealed that with increasing carbon content, the kinetics of transformation of γ phase to deformation stimulated ε-martensite became faster, while that of ε-martensite to α’-martensite was sluggish. We attribute this controversial effect to an increased γ grain size by the microstructural refinement of thermally induced ε-martensite and the reduction of solid solution strengthening effects by the redistribution of solute carbon. In addition, the dependence of deformation-induced ε-martensite on the loading direction differed from that of α’-martensite, and the evolution of α’ morphology was controlled by achieving appropriate levels of strain during stepwise loading. Based on the observations at the surface and inside the bulk after deformation, insights into various deformation-driven displacive phenomena, such as the formation of α’-martensite at the nonintersecting parts of two εinitial bands, the presence of nanotwinned bundles inside austenite, cementite precipitation inside α’-martensite, and the origin of the serrated flow in strain–stress curves, were obtained. Therefore, the present study is able assist in identifying whether the deformation-induced martensitic transformation varied as a function of carbon content and the resulting fracture behavior, thereby enabling us to understand the work-hardening behavior of these steels.


  • High manganese steels
  • Deformation-induced ε-martensite
  • Stepwise tensile loading experiment
  • Transmission electron microscopy
  • Electron backscatter diffraction


Influence of carbon content on the microstructure, martensitic transformation and mechanical properties in austenite/ε-martensite dual-phase Fe–Mn–C steels


Research Highlight
번호 제목 글쓴이 조회 날짜
37 [16.06월] 정운룡 교수 연구실 사진 첨부파일 관리자 2267 2016.07.07
36 [16.06월] 제정호 교수 연구실 사진 첨부파일 관리자 2814 2016.07.07
35 [16.05월] 이장식 교수 연구실 사진 첨부파일 관리자 2872 2016.07.07
34 [16.05월] 이종람 교수 연구실 사진 첨부파일 관리자 2311 2016.07.07
33 [16.03월] 이병주 교수 연구실 사진 첨부파일 관리자 2514 2016.07.07
32 [16.02월] 한세광 교수 연구실 사진 첨부파일 관리자 1877 2016.07.07
31 [16.06월] 조문호 교수 연구실 사진 첨부파일 관리자 1878 2016.06.29
30 [16.02월] 조문호 교수 연구실 첨부파일 관리자 2090 2016.05.11
29 [16.01월] 한세광 교수 연구실 첨부파일 관리자 2908 2016.02.16
28 [15.10월] 이장식 교수 연구실 사진 첨부파일 관리자 2936 2015.10.26
27 [15 09월] 강병우 교수 연구실 첨부파일 관리자 2680 2015.10.26
26 [15.07월] 조문호 교수 연구실 사진 첨부파일 관리자 3042 2015.10.26
25 [15 07월] 정운룡 교수 연구실 사진 첨부파일 관리자 3065 2015.10.22
24 [15 07월] 이종람 교수 연구실 사진 첨부파일 관리자 2379 2015.10.22
23 [15 09월] 제정호 교수 연구실 사진 첨부파일 관리자 3704 2015.10.05
22 [15.07월] 조문호 교수 연구실 사진 첨부파일 관리자 4664 2015.07.20
21 [14.09월] 김종규 교수 연구실 사진 첨부파일 관리자 5119 2014.11.27
20 [14.07월] 제정호 교수 연구실 첨부파일 관리자 4484 2014.11.27
19 [13.10월] 한세광 교수 연구실 사진 첨부파일 관리자 7778 2013.11.11
18 [13.07월] 제정호 교수 연구실 첨부파일 관리자 7155 2013.10.28
처음페이지이전 10 페이지123다음 10 페이지마지막페이지